Home > Graphite for Intumescent Seal

 

 

 

Graphite for Intumescent Seal

 

 

The selfexpansion, high temperature resistance and insulation properties make graphite an excellent sealing material and is widely used.  

Currently there are two major forms: the first one is expandable graphite and rubber materials, inorganic flame retardants 

(aluminum hydroxide), accelerators, vulcanizing agents, reinforcing agents were kneaded into a plastic made  from a variety of the 

expansion seal.  The RESSA RPB Grade fireproof intumescent seals has the great producing of this type seal, details in the website

www.ressatech.com. It mainly used for fire doors, fire windows and other occasions. This seal has consistently blocked the flow of

flue role in the fire. 

 

 

Another is the use of a glass fiber as a carrier adhesive expandable graphite bonded to the carrier, which is mainly used in the 

manufacture of fire doors.Because the high expansion rate of expansible graphite in high temperature conditions, it can be made

of fire bags, fire blocking material, as an effective expansion of flame retardant materials for building fire blocking. Such as sealing

the construction pipeline, in the cable, gas pipeline fire time to prevent the spread of fire.

In order to expand the development and application of expandable graphite in the field of flame retardant, it is necessary to develop

a new type of expandable graphite with wider use range. Several development directions for expandable graphite are as follows: 

1. Low initial expansion temperature and low temperature expandable graphite 

Such expanded graphite began to expand the temperature of 8 to 150 ℃, 600 ℃ expansion volume of 250ml / g, the difficult to 

produce such expandable graphite exists: 

A. Select the appropriate intercalation agent

B. the control and mastery of drying conditions

C. the determination of moisture

D. the solution of environmental problems. At present, the preparation of low temperature expandable graphite has not been reported. 

 


2. Expandable expansive graphite with high initial expansion temperature 

The initial expansion temperature of the expandable graphite at a high initial expansion temperature is 290 to 300 ° C and the expansion 

volume is ≥ 230 ml / g. This type of expandable graphite is mainly used for engineering plastics and rubber flame retardant. RESSA are

 supplying the high quality expandable graphite raw material for the fireproof intumescent seals producing.